ZHANG Dongfang, LIU Guoqiang, CHEN Haoxiang, FAN Zhihong, TIAN Keting. Effect of CaAl-LDH on Service Life of Reinforced Concrete under Marine Environment[J]. Corrosion & Protection, 2024, 45(11): 38-43. DOI: 10.11973/fsyfh240391
|
Calcium aluminum layered double hydroxides (CaAl-LDH) were prepared by co-precipitation and ion exchange method. The effect of CaAl-LDH on the chloride corrosion resistance of rebar in simulated concrete pore solution and the improvement of the service life of reinforced concrete in simulated marine environment were studied by electrochemical test method. The results show that the exchange between CaAl-LDH and chloride ion on the surface of rebar increased the passivation potential of rebar by nearly 200 mV, and the passivation range was expanded. CaAl-LDH could effectively reduce the chloride ion content in concrete, the chloride ion diffusion coefficient and the mass fraction of chloride ion on surface were reduced by 63.6% and 55.3% respectively, and the service life of reinforced concrete structure was prolonged.
| [1] |
刘玉美, 杨浪, 饶峰, 等. 氯离子对海工混凝土钢筋腐蚀的研究进展[J]. 硅酸盐通报, 2023, 42(9), 3059-3074.
LIU Y M, YANG L, RAO F, et al. Research progress of chloride ions on corrosion of marine concrete reinforcement[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(9):3059-3074.
|
| [2] |
侯保荣, 张盾, 王鹏. 海洋腐蚀防护的现状与未来[J]. 中国科学院院刊, 2016, 31(12):1326-1331.
HOU B R, ZHANG D, WANG P. Marine corrosion and protection: current status and prospect[J]. Bulletin of Chinese Academy of Sciences, 2016, 31(12):1326-1331.
|
| [3] |
刘竞, 邓德华, 赵腾龙, 等. 提高海洋环境钢筋混凝土构筑物耐久性措施综述[J]. 腐蚀与防护, 2008, 29(6):329-333.
LIU J, DENG D H, ZHAO T L, et al. A review on measures for prolonging the service life of marine concrete construction[J]. Corrosion & Protection, 2008, 29(6):329-333.
|
| [4] |
秦芳诚, 亓海全, 孟征兵, 等. 海洋工程高抗蚀筋材研究进展[J]. 材料导报, 2022, 36(6):154-160.
QIN F C, QI H Q, MENG Z B, et al. Advances in high corrosion resistant rebar for ocean engineering[J]. Materials Reports, 2022, 36(6):154-160.
|
| [5] |
赵华宇, 杨奔奔, 李莎莎, 等. 金属涂层与有机涂层在混凝土加速腐蚀环境中的腐蚀特性[J]. 腐蚀与防护, 2020, 41(3):26-31
ZHAO H Y, YANG B B, LI S S, et al. Corrosion characteristics of metallic coating and organic coating in concrete accelerated corrosion environment[J]. Corrosion & Protection, 2020, 41(3):26-31.
|
| [6] |
马麒, 蔡景顺, 穆松, 等. 羧酸胺阻锈剂在模拟孔隙液和混凝土中对钢筋的阻锈作用[J]. 材料导报, 2022, 36(23):149-156.
MA Q, CAI J S, MU SONG, et al. Carboxylamine corrosion inhibitor for reinforced steel in simulated concrete pore solution or concrete specimen[J]. Materials Reports, 2022, 36(23):149-156.
|
| [7] |
MIR Z M, BASTOS A, GOMES C, et al. Numerical and experimental analysis of self-protection in reinforced concrete due to application of Mg-Al-NO2 layered double hydroxides[J]. Advanced Engineering Materials, 2020, 22(11):2000398.
|
| [8] |
田玉琬, 文成, 莫湾湾, 等. Zn-Al-NO2 LDH对海洋工程中碳钢钢筋的腐蚀抑制规律[J]. 广东海洋大学学报, 2020, 40(3):122-133.
TIAN Y W, WEN C, MO W W, et al. Corrosion inhibition effect of Zn-Al-NO2 LDH on carbon steel reinforcement in marine engineering[J]. Journal of Guangdong Ocean University, 2020, 40(3):122-133.
|
| [9] |
GOMES C, MIR Z, SAMPAIO R, et al. Use of ZnAl-layered double hydroxide (LDH) to extend the service life of reinforced concrete[J]. Materials, 2020, 13(7):1769.
|
| [10] |
YANG H, XIONG C S, LIU X Y, et al. Application of layered double hydroxides (LDHs) in corrosion resistance of reinforced concrete-state of the art[J]. Construction and Building Materials, 2021, 307:124991.
|
| [11] |
MA G X, XU J X, WANG Z H. Inhibitive effect of sepiolite-supported MgAl-LDH on chloride-induced corrosion of steel in simulated concrete pore solution[J]. Corrosion Science, 2023, 225:111571.
|
| [12] |
文成, 田玉琬, 杨德越, 等. 智能阻锈剂LDH-NO2在钢筋混凝土中的控释机制及缓蚀性能[J]. 工程科学学报, 2022, 44(8):1368-1378.
WEN C, TIAN Y W, YANG D Y, et al. Controlled release mechanism and inhibition performance of smart inhibitor LDH-NO2 in the reinforced concrete structures[J]. Chinese Journal of Engineering, 2022, 44(8):1368-1378.
|
| [13] |
TIAN Y W, WEN C, WANG G, et al. Inhibiting property of nitrite intercalated layered double hydroxide for steel reinforcement in contaminated concrete condition[J]. Journal of Applied Electrochemistry, 2020, 50(8):835-849.
|
| [14] |
XU J X, WEI J F, MA G X, et al. Effect of MgAl-NO2 LDHs inhibitor on steel corrosion in chloride-free and contaminated simulated carbonated concrete pore solutions[J]. Corrosion Science, 2020, 176:108940.
|
| [15] |
周丽娜, 蔡颖, 马财龙, 等. 水滑石复合水泥基材料氯离子吸附能力的研究进展[J]. 硅酸盐通报, 2023, 42(4):1137-1147.
ZHOU L N, CAI Y, MA C L, et al. Research progress on adsorption capacity of hydrotalcite for chloride ions in cement-based materials[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(4):1137-1147.
|
Supported by: Beijing Renhe Information Technology Co., Ltd. 
DownLoad: