JIANG Yong, GONG Jian-ming, ZHOU Rong-rong. Stress Corrosion Cracking of 316L Stainless Steel in NaOH Solution at High Temperatures[J]. Corrosion & Protection, 2008, 29(12): 749-751.
Citation:
JIANG Yong, GONG Jian-ming, ZHOU Rong-rong. Stress Corrosion Cracking of 316L Stainless Steel in NaOH Solution at High Temperatures[J]. Corrosion & Protection, 2008, 29(12): 749-751.
JIANG Yong, GONG Jian-ming, ZHOU Rong-rong. Stress Corrosion Cracking of 316L Stainless Steel in NaOH Solution at High Temperatures[J]. Corrosion & Protection, 2008, 29(12): 749-751.
Citation:
JIANG Yong, GONG Jian-ming, ZHOU Rong-rong. Stress Corrosion Cracking of 316L Stainless Steel in NaOH Solution at High Temperatures[J]. Corrosion & Protection, 2008, 29(12): 749-751.
Stress Corrosion Cracking of 316L Stainless Steel in NaOH Solution at High Temperatures
The SCC behavior of 316L austenitic stainless steel was investigated by using slow strain rate tests (SSRT) in NaOH solutions at high temperatures.The results showed that at high temperatures,even in low NaOH concentration solution,the SCC susceptibility of 316L was apparent.