INHIBITION PERFORMANCE OF COMPOUND INHIBITOR IN 31% NaCl SOLUTION

LIU Fu-guo, DU Min. INHIBITION PERFORMANCE OF COMPOUND INHIBITOR IN 31% NaCl SOLUTION[J]. Corrosion & Protection, 2007, 28(10): 523-525.

Citation:

LIU Fu-guo, DU Min. INHIBITION PERFORMANCE OF COMPOUND INHIBITOR IN 31% NaCl SOLUTION[J]. Corrosion & Protection, 2007, 28(10): 523-525.

Citation:

LIU Fu-guo, DU Min. INHIBITION PERFORMANCE OF COMPOUND INHIBITOR IN 31% NaCl SOLUTION[J]. Corrosion & Protection, 2007, 28(10): 523-525.

Abstract

Inhibition performance of a compound inhibitor (ZnSO4,CaGL,Na(n+2)PnO(3n+1)) for steel G105 in 31% NaCl solution was studied using weight loss,polarization curve and EIS.The compound inhibitor was a mix-type inhibitor.The inhibition efficiency for the steel in the solution was up to 80% at 80 ℃.