WANG Yong-liang, LI Yuan-peng, YANG Guang-nuo, ZHANG Yu, BAI Yao, ZHANG Qi-fu. Microstructure and Anti-corrosion Property of Zn-10% Al-RE Coated Steel Wire[J]. Corrosion & Protection, 2015, 36(5): 419-422.
Citation: WANG Yong-liang, LI Yuan-peng, YANG Guang-nuo, ZHANG Yu, BAI Yao, ZHANG Qi-fu. Microstructure and Anti-corrosion Property of Zn-10% Al-RE Coated Steel Wire[J]. Corrosion & Protection, 2015, 36(5): 419-422.
shu

Microstructure and Anti-corrosion Property of Zn-10% Al-RE Coated Steel Wire

More Information
  • Received Date: June 20, 2014
    Graphical Abstract
    • Abstract
  • Zn-10% Al-RE coated steel wire was made by dual hot dipping method.The chemical compositions of alloy bath and Zn-10% Al-RE coating were analyzed by inductively coupled plasma (ICP) atomic emission spectrometry.The results showed that the content of RE in the Zn-10% Al-RE coating was far less than that in the alloy bath.The microstructures of Zn-10% Al-RE coating and Zn coating were examined and compared by SEM.The anti-corrosion property of both coatings was also analyzed by electrochemical and neural salt spraying (NSS) methods.The results showed that the corrosion current of Zn-10% Al-RE coating was about one twentieth of that of zinc coatings.The weight loss of Zn-10% Al-RE coating was one third of that of Zn coating,which proved that the anti-corrosion property of Zn-10% Al-RE coating was highly superior to that of Zn coating.
    • FullText(HTML)
    • References (8)
  • [1]
    李胜利.镀锌钢丝与锌基合金复合的界面特征[J].金属热处理,2000,36(3):9-10.
    [2]
    唐建平.热镀锌钢丝锌层面质量的研究[J].金属制品,2005,31(3):13-14.
    [3]
    徐洪林,俞国森,林晓晟.镀锌线材制品防白锈的探讨[J].金属制品,2002,28(2):48-51.
    [4]
    谭澄宇,魏修宇,陈准.Zn-5% Al-RE镀层耐蚀性能的研究[J].电镀与环保,2002,22(5):29-32.
    [5]
    蒋治鑫,李广龄.Zn-5% Al-RE合金(Galfan)镀层钢丝的开发应用[J].金属制品,2001,27(2):4-7.
    [6]
    张建国,高飞,王子昆.超高压输电线路Zn-5% Al-混合稀土合金镀层钢丝及钢绞线的生产技术研究[J].天津冶金,2007,141(3):3-6.
    [7]
    李广龄.Zn-5% Al-RE合金镀液的浸润性及其对表面质量的影响[J].金属制品,1999,25(5):8-10.
    [8]
    黄跃进.Zn-5% Al-RE合金镀层钢丝的形貌和耐腐蚀分析[J].热处理,2003,18(4):28-31.
    • Related Articles

Catalog

    Get Citation
    PDF
    XML
    Article views (5) PDF downloads (2) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    References

    Corrosion & Protection

    Address：99 Handan Road, ShanghaiPost Code: 200437

    Tel：021-65556775-290Email:cp@mat-test.com

    沪ICP备17055736号-5

    Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return