HE Jia-sheng, CUI Hao-xuan, ZHU Xiao-ming, LU Yuan-ming, WU Jian-ping, ZHU Guang-qiang. INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT[J]. Corrosion & Protection, 2007, 28(11): 559-561.
Citation:
HE Jia-sheng, CUI Hao-xuan, ZHU Xiao-ming, LU Yuan-ming, WU Jian-ping, ZHU Guang-qiang. INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT[J]. Corrosion & Protection, 2007, 28(11): 559-561.
HE Jia-sheng, CUI Hao-xuan, ZHU Xiao-ming, LU Yuan-ming, WU Jian-ping, ZHU Guang-qiang. INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT[J]. Corrosion & Protection, 2007, 28(11): 559-561.
Citation:
HE Jia-sheng, CUI Hao-xuan, ZHU Xiao-ming, LU Yuan-ming, WU Jian-ping, ZHU Guang-qiang. INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT[J]. Corrosion & Protection, 2007, 28(11): 559-561.
INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT
The failure of bolts made of 35CrMoA steel was studied by a self designed experimental approach.The analysis of component,microstructure fracture morphology of 35CrMoA steel and stress concentration at crack tip had been finished.The stress corrosion cracking would occur if the stress of the bolts made of 35CrMoA steel used in wet H2S environment is greater than a certain value.