CHEN Huo-ping, LI Li-qing, LI Min. Film Forming Analysis and Multifunctional Phosphating Solution for Iron and Steel at Normal Temperature[J]. Corrosion & Protection, 2008, 29(12): 772-773.
Citation:
CHEN Huo-ping, LI Li-qing, LI Min. Film Forming Analysis and Multifunctional Phosphating Solution for Iron and Steel at Normal Temperature[J]. Corrosion & Protection, 2008, 29(12): 772-773.
CHEN Huo-ping, LI Li-qing, LI Min. Film Forming Analysis and Multifunctional Phosphating Solution for Iron and Steel at Normal Temperature[J]. Corrosion & Protection, 2008, 29(12): 772-773.
Citation:
CHEN Huo-ping, LI Li-qing, LI Min. Film Forming Analysis and Multifunctional Phosphating Solution for Iron and Steel at Normal Temperature[J]. Corrosion & Protection, 2008, 29(12): 772-773.
Film Forming Analysis and Multifunctional Phosphating Solution for Iron and Steel at Normal Temperature
A new phosphating solution was developed.The phosphate coating formed in this solution was smooth and gray,and had high adhesion,and could withstand CuSO4 corrosion test for more than 2 mins and NaCl immersion test for more than 6 h.